해외표준 상세정보

관심표준 등록 : 표준업데이트 시 알림서비스

제공형태 더보기

  • KS

    구판

    판매

    ASTM F519-12a

    Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating/Coating Processes and Service Environments
    • 발행일 : 2012-11-15
    • 발행기관 : ASTM
    즐겨찾기 장바구니 담기
    닫기

    상품이 장바구니에 담겼습니다.

    장바구니로 이동

    • [영어]PDF 144,300원

    • [영어]PRINT 144,300원

상세정보

분야 15.03 : 공간시물레이션; 항공우주재료; 고율섬유와 합성물
적용범위

1.1 This test method describes mechanical test methods and defines acceptance criteria for coating and plating processes that can cause hydrogen embrittlement in steels. Subsequent exposure to chemicals encountered in service environments, such as fluids, cleaning treatments or maintenance chemicals that come in contact with the plated/coated or bare surface of the steel, can also be evaluated.

1.2 This test method is not intended to measure the relative susceptibility of different steels. The relative susceptibility of different materials to hydrogen embrittlement may be determined in accordance with Test Method F1459 and Test Method F1624.

1.3 This test method specifies the use of air melted AISI E4340 steel per SAE AMS-S-5000 (formerly MIL-S-5000) heat treated to 260 to 280 ksi (pounds per square inch ×1000) as the baseline. This combination of alloy and heat treat level has been used for many years and a large database has been accumulated in the aerospace industry on its specific response to exposure to a wide variety of maintenance chemicals, or electroplated coatings, or both. Components with ultimate strengths higher than 260 to 280 ksi may not be represented by the baseline. In such cases, the cognizant engineering authority shall determine the need for manufacturing specimens from the specific material and heat treat condition of the component. Deviations from the baseline shall be reported as required by 12.1.2. The sensitivity to hydrogen embrittlement shall be demonstrated for each lot of specimens as specified in 9.5.

1.4 Test procedures and acceptance requirements are specified for seven specimens of different sizes, geometries, and loading configurations.

1.5 Pass/Fail Requirements—For plating/coating processes, specimens must meet or exceed 200 h using a sustained load test (SLT) at the levels shown in Table 3.

TABLE 1 Lot Acceptance Criteria for Notched Specimens

Type

Item

Sampling of
Each Lot

Requirement/Method

1

Tensile Strength

4 each

Test Method E8. Tensile strength of each specimen must be within 10 ksi of the average.

1 

HardnessA

5 %

51 to 53 HRC per Test Methods E18.
 Round the average of
 three readings per
 specimen per Practice
 E29.

1 

Dimensions

100 %

Meet tolerances of
 corresponding
 drawings. Notch
 dimension verified with
 shadow graphic
 projection at 50 to
 100× or equivalent.

1 

Notched Fracture Strength (NFS)

10 ea

Test Methods E8/E8M. NFS of each specimen
 must be within 10 ksi
 of the average.

1c

Self-loading
 notched round
 specimen bend
 fixture, Fig. A2.7

10 ea

Alternate: The number of
 turns of the loading
 bolt, which is required
 to produce fracture in
 each specimen, must be
 within 5 % of the
 average.

1d

Self-loading
 notched C-Ring
 bend fixture,
 Fig. A2.8

10 ea

Alternate: The change in
 diameter at fracture
 load for each specimen
 must be within 0.008
 inches of the average.

A If the hardness requirements of any of the sampled specimens are not satisfied, only those specimens of the lot that are individually inspected for conformance to these requirements shall be used for testing.
TABLE 2 Electroplating Bath Compositions and Operating Conditions for Sensitivity Test

Item

Treatment A

Treatment B

Bath composition:

Range

Optimum

 

 Cadmium (as CdO)

2.9 to 5.5 oz/gal (22 to 41 g/L)

4.5 oz/gal (33.7 g/L)

same as Treatment A

 Total Sodium cyanide
  (NaCN)

12.0 to 16.0 oz/gal (89.9 to 120 g/L)

14 oz/gal (104 g/L)

same as Treatment A

 Ratio NaCN to CdO

2.8/1 to 6.0/1

3.0/1

same as Treatment A

 pH

12.0 or greater

12.0

same as Treatment A

 Temperature

70–90°F (21–32°C)

75°F (24°C)

same as Treatment A

 Sodium hydroxide
  (NaOH)A

1.0 to 3.2 oz/gal (7.5 to 24.0 g/L)

2.5 oz/gal (18.7 g/L)

same as Treatment A

 Brightener such as
  Colcad 100B or
  equivalent

Manufacturer's suggested range

None

 Electroplating current

10 A/ft2  (108 A/m2)

60 A/ft2  (645 A/m 2)

 Electroplating time

30 minutes

6 minutes

Baking

 

 

 

 Baking temperature

375 ± 25°F (190 ± 14°C)

same as Treatment A

 Baking time: Type 1
  Specimen

Do Not Bake

23 h

 Baking time: Type 2a
  Specimen

8 h

23 h

Chromate TreatmentC

Yes

same as Treatment A

A Addition of sodium hydroxide may not be required on solution makeup, since the addition of 1 oz/gal of cadmium oxide is equivalent to 0.6 oz/gal of free hydroxide.
B The sole source of manufacture of Colcad 100 known to the committee at this time is Columbia Chemical in Brunswick, Ohio, www.columbiachemical.com. If you are aware of alternative manufacturers, please provide this information to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of the responsible technical committee, which you may attend.
C After baking, the specimens shall be dipped into any appropriate chromate conversion coating solution for minimum time that will produce an adherent and continuous coating as described in AMS-QQ-P-416 Type II.
TABLE 3 Pass/Fail Loading Requirements of Test Specimens

Type 1a, 1b, 1c, 1d, 1e

75 % of the tensile or bend NFS (Table 1).

Type 2a

92 % of the Test Methods E8/E8M, E4 ultimate strength, obtained by deflecting a 2.300-inch diameter O-Ring specimen with a 2.525-inch stressing bar.


1.5.1 The loading conditions and pass/fail requirements for service environments are specified in Annex A5.

1.5.2 If approved by the cognizant engineering authority, a quantitative, accelerated (≤ 24 h) incremental step-load (ISL) test as defined in Annex A3 may be used as an alternative to SLT.

1.6 This test method is divided into two parts. The first part gives general information concerning requirements for hydrogen embrittlement testing. The second is composed of annexes that give specific requirements for the various loading and specimen configurations covered by this test method (see section 9.1 for a list of types) and the details for testing service environments.

1.7 The values stated in the foot-pound-second (fps) system in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

1.8 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
국제분류(ICS)코드
페이지수 18
Edition 12a

이력정보

No. 표준번호 표준명 발행일 상태
1 ASTM F519-23상세보기 Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating/Coating Processes and Service Environments 2023-12-01 표준
2 ASTM F519-23 REDLINE상세보기 Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating/Coating Processes and Service Environments 2023-12-01 표준
3 ASTM F519-18상세보기 Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating/Coating Processes and Service Environments 2018-11-01 구판
4 ASTM F519-18 REDLINE상세보기 Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating/Coating Processes and Service Environments 2018-11-01 구판
5 ASTM F519-17a상세보기 Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating/Coating Processes and Service Environments 2017-12-01 구판
6 ASTM F519-17상세보기 Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating/Coating Processes and Service Environments 2017-03-01 구판
7 ASTM F519-13상세보기 Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating/Coating Processes and Service Environments 2013-12-01 구판
8 ASTM F519-12a상세보기 Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating/Coating Processes and Service Environments 2012-11-15 구판
9 ASTM F519-12상세보기 Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating/Coating Processes and Service Environments 2012-06-01 구판
10 ASTM F519-10상세보기 Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating/Coating Processes and Service Environments 2010-12-01 구판
11 ASTM F519-08상세보기 Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating/Coating Processes and Service Environments 2008-05-01 구판
12 ASTM F519-06e2상세보기 Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating/Coating Processes and Service Environments 2006-07-01 구판
13 ASTM F519-06e1상세보기 Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating/Coating Processes and Service Environments 2006-07-01 구판
14 ASTM F519-06상세보기 Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating/Coating Processes and Service Environments 2006-07-01 구판
15 ASTM F519-05상세보기 Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating Processes and Service Environments 2005-04-01 구판
16 ASTM F519-97e2상세보기 Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating Processes and Service Environments 2000-06-26 구판

관련상품

  • 관련상품이 존재하지 않습니다.

다른 사람이 함께 구입한 상품

  • 함께 구입한 상품이 존재하지 않습니다.

추천 상품

제공형태 닫기

  • PDF :

    직접 파일 다운로드 및 인쇄(마이페이지 확인)

  • 보안PDF :

    직접 파일 다운로드 및 인쇄(마이페이지 확인)* 단, 파일이동 및 복사 불가, 1회 다운로드 및 인쇄가능

  • PRINT :

    인쇄본 우편발송, 2~3일 소요(PDF파일 미제공)

  • BOOK :

    인쇄본 우편발송, 2~3일 소요(PDF파일 미제공)

  • ZIP :

    압축파일형태로 제공 (PDF, HTML, TXT, XLS 등으로 구성), 직접 파일 다운로드(마이페이지 확인)

  • CD/DVD :

    직접 파일 다운로드 및 인쇄(마이페이지 확인)

  • DB :

    별도 정보 제공

  • HARDCOPY :

    해외 배송 상품, 최대 3주 소요

  • 바인더 :

    바인더 우편발송, 2~3일 소요

  • 온라인구독 :

    WEB 접속 후 실시간 열람, 출력(1년간)