분야 | 01.03 : 철강-강판, 강대 및 강선 |
---|---|
적용범위 | 1.1?The purpose of these test methods is to allow detection of the presence of intermetallic phases in certain duplex stainless steels as listed in Table 1, Table 2, and Table 3 to the extent that toughness or corrosion resistance is affected significantly. These test methods will not necessarily detect losses of toughness or corrosion resistance attributable to other causes. Similar test methods for other duplex stainless steels are described in Test Method A1084, but the procedures described in this standard differ significantly from Test Methods A, B, and C in A1084. 1.2?Duplex (austenitic-ferritic) stainless steels are susceptible to the formation of intermetallic compounds during exposures in the temperature range from approximately 600 to 1750?°F (320 to 955?°C). The speed of these precipitation reactions is a function of composition and thermal or thermomechanical history of each individual piece. The presence of these phases is detrimental to toughness and corrosion resistance. 1.3?Correct heat treatment of duplex stainless steels can eliminate these detrimental phases. Rapid cooling of the product provides the maximum resistance to formation of detrimental phases by subsequent thermal exposures. 1.4?Compliance with the chemical and mechanical requirements for the applicable product specification does not necessarily indicate the absence of detrimental phases in the product. 1.5?These test methods include the following: 1.5.1?Test Method A?Sodium Hydroxide Etch Test for Classification of Etch Structures of Duplex Stainless Steels (Sections 3 ? 7). 1.5.2?Test Method B?Charpy Impact Test for Classification of Structures of Duplex Stainless Steels (Sections 8 ? 13). 1.5.3?Test Method C?Ferric Chloride Corrosion Test for Classification of Structures of Duplex Stainless Steels (Sections 14 ? 20). 1.6?The presence of detrimental intermetallic phases is readily detected in all three tests, provided that a sample of appropriate location and orientation is selected. Because the occurrence of intermetallic phases is a function of temperature and cooling rate, it is essential that the tests be applied to the region of the material experiencing the conditions most likely to promote the formation of an intermetallic phase. In the case of common heat treatment, this region will be that which cooled most slowly. Except for rapidly cooled material, it may be necessary to sample from a location determined to be the most slowly cooled for the material piece to be characterized. 1.7?The tests do not determine the precise nature of the detrimental phase but rather the presence or absence of an intermetallic phase to the extent that it is detrimental to the toughness and corrosion resistance of the material. 1.8?Examples of the correlation of thermal exposures, the occurrence of intermetallic phases, and the degradation of toughness and corrosion resistance are given in Appendix X1 and Appendix X2. 1.9?The values stated in either inch-pound or SI units are to be regarded as the standard. The values given in parentheses are for information only. 1.10?This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.11?This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. |
국제분류(ICS)코드 | 77.040.99 : 기타 금속 시험 방법 |
페이지수 | 10 |
Edition | 23 |
No. | 표준번호 | 표준명 | 발행일 | 상태 |
---|---|---|---|---|
1 | ASTM A923-23 | Standard Test Methods for Detecting Detrimental Intermetallic Phase in Duplex Austenitic/Ferritic Stainless Steels | 2023-05-15 | 표준 |
2 | ASTM A923-23 REDLINE | Standard Test Methods for Detecting Detrimental Intermetallic Phase in Duplex Austenitic/Ferritic Stainless Steels | 2023-05-15 | 표준 |
3 | ASTM A923-22 | Standard Test Methods for Detecting Detrimental Intermetallic Phase in Duplex Austenitic/Ferritic Stainless Steels | 2022-06-01 | 구판 |
4 | ASTM A923-22 REDLINE | Standard Test Methods for Detecting Detrimental Intermetallic Phase in Duplex Austenitic/Ferritic Stainless Steels | 2022-06-01 | 구판 |
5 | ASTM A923-14 REDLINE | Standard Test Methods for Detecting Detrimental Intermetallic Phase in Duplex Austenitic/Ferritic Stainless Steels | 2014-03-01 | 구판 |
6 | ASTM A923-14 | Standard Test Methods for Detecting Detrimental Intermetallic Phase in Duplex Austenitic/Ferritic Stainless Steels | 2014-03-01 | 구판 |
7 | ASTM A923-08 | Standard Test Methods for Detecting Detrimental Intermetallic Phase in Duplex Austenitic/Ferritic Stainless Steels | 2008-10-01 | 구판 |
8 | ASTM A923-06 | Standard Test Methods for Detecting Detrimental Intermetallic Phase in Duplex Austenitic/Ferritic Stainless Steels | 2006-05-01 | 구판 |
9 | ASTM A923-03 | Standard Test Methods for Detecting Detrimental Intermetallic Phase in Wrought Duplex Austenitic/Ferritic Stainless Steels | 2003-10-01 | 구판 |
10 | ASTM A923-01e1 | Standard Test Methods for Detecting Detrimental Intermetallic Phase in Wrought Duplex Austenitic/Ferritic Stainless Steels | 2001-09-10 | 구판 |
11 | ASTM A923-98 | Standard Test Methods for Detecting Detrimental Intermetallic Phase in Wrought Duplex Austenitic/Ferritic Stainless Steels | 2001-09-10 | 구판 |
12 | ASTM A923-01 | Standard Test Methods for Detecting Detrimental Intermetallic Phase in Wrought Duplex Austenitic/Ferritic Stainless Steels | 2001-09-10 | 구판 |
관련상품이 존재하지 않습니다.
ASTM E23-23a - Standard Test Methods for Notched Bar Impact Testing of Metallic Materials 상세보기
ASTM E92-23 - Standard Test Methods for Vickers Hardness and Knoop Hardness of Metallic Materials 상세보기
JIS Z 2242:2023 - Method for Charpy pendulum impact test of metallic materials 상세보기
ASTM E562-19e1 - Standard Test Method for Determining Volume Fraction by Systematic Manual Point Count 상세보기
ASTM E10-23 - Standard Test Method for Brinell Hardness of Metallic Materials 상세보기
IEC TS 63134:2020 - Active assisted living (AAL) use cases 상세보기
IEC 60034-5:2020 RLV - Rotating electrical machines - Part 5: Degrees of protection provided by the integral design of rotating electrical machines (IP code) - Classification 상세보기
KS B ISO TS 25740-1 - 에스컬레이터 및 무빙워크에 대한 안전요건 — 제1부: 세계공통 필수 안전요건(GESRs) 상세보기
KS B ISO TS 8100-21 - 승객 및 화물 운송용 엘리베이터 —제21부: 세계공통 필수안전요건(GESRs)을 충족하는 세계공통 안전 파라미터(GSPs) 상세보기
KS C IEC TS 62872 - 산업 시설과 스마트 그리드 사이의 산업 공정 측정, 제어 및 자동화 시스템 인터페이스 상세보기